Gromax CCP PBT 4815-NCB 15% Glass Fiber Filled
[2019-06-06 09:25:51]
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
水分吸收 | 0.0300 % @Time 86400 sec | 0.0300 % @Time 24.0 hour | ASTM D570 |
线性成型收缩率 | 0.0030 - 0.0060 cm/cm @Thickness 1.60 mm | 0.0030 - 0.0060 in/in @Thickness 0.0630 in | horizontal; ASTM D955 |
0.014 - 0.020 cm/cm @Thickness 1.60 mm | 0.014 - 0.020 in/in @Thickness 0.0630 in | vertical; ASTM D955 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
洛氏硬度(R 级) | 120 | 120 | ASTM D785 |
抗张强度 | 96.1 MPa | 13900 psi | ASTM D638 |
伸长率 (断裂) | 3.8 % | 3.8 % | ASTM D638 |
弯曲强度 | 142 MPa | 20600 psi | ASTM D790 |
弯曲模量 | 5.39 GPa | 782 ksi | ASTM D790 |
悬壁梁缺口冲击强度 | >= 0.628 J/cm @Thickness 6.35 mm | >= 1.18 ft-lb/in @Thickness 0.250 in | ASTM D256 |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
体积电阻率 | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
表面电阻 | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
介电常数 | 3.3 @Frequency 60.0 Hz | 3.3 @Frequency 60.0 Hz | ASTM D150 |
介电强度 | 23.0 kV/mm @Thickness 2.00 mm | 584 kV/in @Thickness 0.0787 in | ASTM D149 |
耗散因数 | 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 |
耐电弧性 | 90 sec | 90 sec | ASTM D495 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线性热膨胀系数 | 55.0 µm/m-°C | 30.6 µin/in-°F | ASTM D696 |
熔融温度 | 225 °C | 437 °F | DSC |
载荷下热变形温度(0.46 MPa) | 220 °C | 428 °F | ASTM D648 |
载荷下热变形温度(1.8 MPa) | 195 °C | 383 °F | ASTM D648 |
可燃性(UL94) | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in |
加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
加工温度 | 240 - 270 °C | 464 - 518 °F | |
射嘴温度 | 260 - 270 °C | 500 - 518 °F | |
模具温度 | 40.0 - 120 °C | 104 - 248 °F | suitable temperature 60-80°C |
注射压力 | 50.0 - 120 MPa | 7250 - 17400 psi | |
保压 | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
背压 | 0.000 - 0.300 MPa | 0.000 - 43.5 psi | |
螺杆转速 | 60 - 120 rpm | 60 - 120 rpm | to be chosen in such a way that plasticizing time is just within cooling time |
材料描述 | 测试方法 | |
---|---|---|
注射速率 | middle-fast |